槽钢理论重量表:
| 品名 | 规格 | 高度 | 腿宽 | 腰厚 | 理重 |
| 热镀锌槽钢 | 5# | 50 | 37 | 4.5 | 5.438 |
| 热镀锌槽钢 | 6.3# | 63 | 40 | 4.8 | 6.634 |
| 热镀锌槽钢 | 8# | 80 | 43 | 5 | 8.045 |
| 热镀锌槽钢 | 10# | 100 | 48 | 5.3 | 10.007 |
| 热镀锌槽钢 | 12# | 120 | 53 | 5.5 | 12.059 |
| 热镀锌槽钢 | 12.6# | 126 | 53 | 5.5 | 12.318 |
| 热镀锌槽钢 | 14#a | 140 | 58 | 6 | 14.535 |
| 热镀锌槽钢 | 14#b | 140 | 60 | 8 | 16.733 |
| 热镀锌槽钢 | 16#a | 160 | 63 | 6.5 | 17.24 |
| 热镀锌槽钢 | 16#b | 160 | 65 | 8.5 | 19.752 |
| 热镀锌槽钢 | 18#a | 180 | 68 | 7 | 20.174 |
| 热镀锌槽钢 | 18#b | 180 | 70 | 9 | 23 |
| 热镀锌槽钢 | 20#a | 200 | 73 | 7 | 22.637 |
| 热镀锌槽钢 | 20#b | 200 | 75 | 9 | 25.777 |
| 热镀锌槽钢 | 22#a | 220 | 77 | 7 | 24.999 |
| 热镀锌槽钢 | 22#b | 220 | 79 | 9 | 28.453 |
| 热镀锌槽钢 | 25#a | 250 | 78 | 7 | 27.41 |
| 热镀锌槽钢 | 25#b | 250 | 80 | 9 | 31.335 |
| 热镀锌槽钢 | 25#c | 250 | 82 | 11 | 35.26 |
| 热镀锌槽钢 | 28#a | 280 | 82 | 7.5 | 31.427 |
| 热镀锌槽钢 | 28#b | 280 | 84 | 9.5 | 35.832 |
| 热镀锌槽钢 | 28#c | 280 | 86 | 11 | 40.219 |
| 热镀锌槽钢 | 32#a | 320 | 88 | 8 | 38.083 |
| 热镀锌槽钢 | 32#b | 320 | 90 | 10 | 43.107 |
| 热镀锌槽钢 | 32#c | 320 | 92 | 12 | 48.131 |
| 热镀锌槽钢 | 36#a | 360 | 96 | 9 | 47.814 |
| 热镀锌槽钢 | 36#b | 360 | 98 | 11 | 53.466 |
| 热镀锌槽钢 | 36#c | 360 | 100 | 13 | 59.118 |
| 热镀锌槽钢 | 40#a | 400 | 100 | 10 | 58.928 |
| 热镀锌槽钢 | 40#b | 400 | 102 | 12.5 | 65.208 |
| 热镀锌槽钢 | 40#c | 400 | 104 | 14.5 | 71.488 |
莎伦法：1939年美国莎伦公司投产一台新型的热镀锌机组，所以也叫莎伦法。该法是在退火炉内向带钢喷射氯化氢气体并使带钢达到再结晶温度，所以也称为气体酸洗法。采用氯化氢气体酸洗，不但能去除带钢表面的氧化皮，而且同时去除了带钢表面的油脂，由于带钢表面被氧化气体腐蚀，形成麻面，所以使用莎伦法所得到的镀层粘附性特别好。但是由于设备腐蚀严重，由此造成很高的设备维修和更新费用。因而此种方法很少被采用。
改良森吉米：它是一种更优越的热镀锌工艺方法;它把森吉米尔法中各自独立的氧化炉和还原炉由一个截面积较小的过道连接起来，这样包括预热炉、还原炉和冷却段在内的整个退火炉构成一个有机整体。实践证明，该法具有许多优点:优质、高产、低耗、等优点已逐渐被人们所认识。其发展速度非常快，1965年以来新建的作业线几乎全部采用了这种方法，近年来老的森吉米尔机组也大都按照此方法进行了改造。